Aluminum alloy 6061 is a versatile and widely used heat-treatable alloy that belongs to the 6000 series of aluminum alloys. It is known for its excellent machinability, good strength-to-weight ratio, and high corrosion resistance.
Properties: |
---|
Density: 2.70 g/cm³ Melting Point: 580°C (1075°F) Tensile Strength: Varies based on temper and thickness. Yield Strength: Varies based on temper and thickness. Elongation at Break: Varies based on temper and thickness. Modulus of Elasticity: Approximately 68.9 GPa (10,000 ksi) Thermal Conductivity: 167 W/m·K |
Details and Characteristics: |
Anodizing Compatibility: 6061 aluminum is well-suited for anodizing treatments to enhance its surface properties. Strength-to-Weight Ratio: 6061 alloy provides a high strength-to-weight ratio, making it a popular choice for structural applications. Machinability: It has excellent machinability, making it suitable for various machining operations, including milling, drilling, and turning. Weldability: 6061 aluminum has good weldability, although precautions should be taken to avoid cracking. It responds well to various welding techniques. |
Alloy: 6061 Aluminium Alloy
Temper:
O H14 H24 H18 / T351 T3 T4 T651 T6 / H14 H24 H26 H16 / H32 H111 H321 H116 H112 / T6 T651 / T651 T6 T7451
Thickness: 0.2mm-300mm
Width: 500mm-3000mm
Standard: GB/ 3880-2012 ASTMB209 EN485
Surface Treatment: Mill finish / Brush polish
PVC Coated: One side or two side PVC
MOQ: The inventory has no MOQ
Packing: Standard Export Packing
Port of Dispatch: It depends on the supplier's location and shipping arrangements
Delivery Time: The inventory is 5-7 days . 25-30 days for customized products
Payment: TT / LC / TT+LC
Chemical Composition |
|
Aluminium (Al): | 97.9% |
---|---|
Iron (Fe): | 0.70% |
Manganese (Mn): | 0.15% |
Magnesium (Mg): | 1.0% - 1.2% |
Zinc (Zn): | 0.25% |
Silicon (Si): | 0.40% - 0.80% |
Copper (Cu): | 0.15% - 0.40% |
Titanium (Ti): | 0.15% |
Chromium (Cr): | 0.04% - 0.35% |
other | 0.05%(each) 0.15(total) |