2014 Aluminium Flat Bar
2014 aluminium flat bars can vary based on the manufacturer and customer requirements. Using 2014 aluminium for a specific application, it's advisable to consult with the relevant standards and specifications to ensure the alloy's suitability for the intended use.
| Details and Characteristics: |
|---|
|
High Strength:2014 aluminium is known for its high strength, and it is one of the strongest heat-treatable aluminium alloys. It offers excellent strength-to-weight ratio. Heat Treatable:2014 is a heat-treatable alloy, and its mechanical properties can be significantly improved through heat treatment processes. Formability:While it has good machinability, 2014 may have reduced formability compared to some other aluminium alloys. It is essential to consider the forming requirements for the intended application. Surface Finish:The surface finish of 2014 aluminium flat bar can vary based on manufacturing processes. It can be finished to achieve different levels of smoothness or roughness. Corrosion Resistance:2014 aluminium has moderate corrosion resistance. However, its primary strength lies in its mechanical properties rather than corrosion resistance. Welding:Welding of 2014 aluminium can be challenging, and it may require special considerations. It is essential to follow appropriate welding procedures. |
2014 Aluminium Flat Bars
Alloy : 2014 Aluminium Alloy
Temper:
O H14 H18 / T351 T3 T4 / H24 H26 H16 / H32 H111 H321 H116 H112 / T6 T651 / T7451 T6511
Diameter: 10mm-500mm
Length: 500mm-6000mm
Standard: GB/T 3880-2012 ASTMB209 EN485
Surface Treatment: Mill Finish / Brush PSolish / Bright Finish
MOQ: The inventory has no MOQ 2mt-3mt
Packing: Standard Export Packing
Port of Dispatch: It depends on the supplier's location and shipping arrangements
Delivery Time: The inventory is 5-7 days . 25-30 days for customized products
Payment: TT / LC / TT+LC
Applications:
Aerospace components
Aircraft structures
Automotive parts
Precision parts and components
Structural components requiring high strength
Chemical Composition |
|
| Aluminium (Al): | 90.7-94.7% |
|---|---|
| Copper (Cu): | 3.9-5.0% |
| Iron (Fe): | 0.50% |
| Silicon (Si): | 0.50-1.2% |
| Manganese (Mn): | 1.2-1.8% |
| Magnesium (Mg): | 1.2-1.8% |
| Zinc (Zn): | 1.2-1.8% |
| Titanium (Ti): | 0.20-0.8% |
| Other | 0.05%(each) 0.15(total) |