2017 Aluminium Flat Bar
2017 aluminium flat bars can vary based on the manufacturer and customer requirements. Using 2017 aluminium for a specific application, it's advisable to consult with the relevant standards and specifications to ensure the alloy's suitability for the intended use.
| Details and Characteristics: |
|---|
|
High Strength:2017 aluminium is known for its high strength, and it is a heat-treatable alloy. It offers good mechanical properties, including excellent machinability. Heat Treatable:2017 is a heat-treatable alloy, and its mechanical properties can be improved through heat treatment processes. Machinability:2017 aluminium has excellent machinability, making it suitable for applications where machining precision and speed are essential. Formability:While it has good machinability, 2017 may have reduced formability compared to some other aluminium alloys. It is essential to consider the forming requirements for the intended application. Surface Finish:The surface finish of 2017 aluminium flat bar can vary based on manufacturing processes. It can be finished to achieve different levels of smoothness or roughness. Corrosion Resistance:While it exhibits reasonable corrosion resistance, 2017 aluminium is not as corrosion-resistant as some other aluminium alloys. It may be susceptible to corrosion in certain environments. Welding:Welding of 2017 aluminium can be challenging, and it may require special considerations. It is essential to follow appropriate welding procedures. |
2017 Aluminium Flat Bars
Alloy : 2017 Aluminium Alloy
Temper:
O H14 H18 / T351 T3 T4 / H24 H26 H16 / H32 H111 H321 H116 H112 / T6 T651 / T7451 T6511
Diameter: 10mm-500mm
Length: 500mm-6000mm
Standard: GB/T 3880-2012 ASTMB209 EN485
Surface Treatment: Mill Finish / Brush PSolish / Bright Finish
MOQ: The inventory has no MOQ 2mt-3mt
Packing: Standard Export Packing
Port of Dispatch: It depends on the supplier's location and shipping arrangements
Delivery Time: The inventory is 5-7 days . 25-30 days for customized products
Payment: TT / LC / TT+LC
Applications:
Aerospace components
Aircraft fittings
Structural components
High-stress applications
Automotive parts
Screw machine products
Chemical Composition |
|
| Aluminium (Al): | 91.0-92.8% |
|---|---|
| Copper (Cu): | 3.5-4.5% |
| Iron (Fe): | 0.50% |
| Manganese (Mn): | 1.2-2.0% |
| Magnesium (Mg): | 1.5-2.3% |
| Zinc (Zn): | 0.20% |
| Chromium (Cr): | 0.10-0.30% |
| Titanium (Ti): | 0.20% |
| Other | 0.05%(each) 0.15(total) |