2011 Aluminium Plate
Aluminum alloy 2011 is a free-machining grade with high mechanical strength. It belongs to the 2000 series aluminum alloys, which are known for their excellent machinability.
| Properties: |
|---|
|
Density: 2.78 g/cm³ Melting Point: 535°C (995°F) Tensile Strength: 379 MPa (55,000 psi) Yield Strength: 221 MPa (32,000 psi) Elongation at Break: 15% Modulus of Elasticity: 71 GPa (10,300 ksi) Thermal Conductivity: 201 W/m·K Machinability (ASTM B311): 90% (compared to 1212 steel) |
| Details and Characteristics: |
|
High Machinability:2011 aluminum alloy is known for its excellent machinability, making it a preferred choice for parts that require intricate machining. Good Mechanical Properties:It offers good strength, especially when compared to other free-machining aluminum alloys. Limited Corrosion Resistance:While it provides reasonable corrosion resistance, it is not as corrosion-resistant as other aluminum alloys, such as the 6000 or 5000 series. Heat Treatable:The alloy can be heat-treated to improve its mechanical properties. Applications:Commonly used in applications where machining is a critical factor, such as in the production of intricate parts for the automotive and aerospace industries. |
2011 Aluminium Plates
Alloy : 2011 Aluminium Alloy
Temper :
O H14 H24 H18 / T351 T3 T4 T651 T6 / H14 H24 H26 H16 / H32 H111 H321 H116 H112 / T6 T651 / T651 T6 T7451
Thickness : 0.2mm-300mm
Width : 500mm-3000mm
Standard : GB/ 3880-2012 ASTMB209 EN485
Surface Treatment : Mill finish / Brush polish
PVC Coated : One side or two side PVC
MOQ : The inventory has no MOQ
Packing : Standard Export Packing
Port of Dispatch : It depends on the supplier's location and shipping arrangements
Delivery Time : The inventory is 5-7 days . 25-30 days for customized products
Payment : TT / LC / TT+LC
Chemical Composition |
|
| Aluminium (Al): | 91.7% |
|---|---|
| Copper (Cu): | 6.1% |
| Iron (Fe): | 0.50% |
| Lead (Pb): | 0.70% - 1.20% |
| Bismuth (Bi): | 0.20% - 0.60% |
| Others: | 0.5%(each) 0.15%(total) |