Aluminium 2014 Flat Bar in T651 Temper Strong and Machinable
alu flat bar

2014 Aluminium Flat Bar

2014 aluminium flat bars can vary based on the manufacturer and customer requirements. Using 2014 aluminium for a specific application, it's advisable to consult with the relevant standards and specifications to ensure the alloy's suitability for the intended use.


Details and Characteristics:

Heat Treatable:2014 is a heat-treatable alloy, and its mechanical properties can be significantly improved through heat treatment processes.

Welding:Welding of 2014 aluminium can be challenging, and it may require special considerations. It is essential to follow appropriate welding procedures.

Corrosion Resistance:2014 aluminium has moderate corrosion resistance. However, its primary strength lies in its mechanical properties rather than corrosion resistance.

High Strength:2014 aluminium is known for its high strength, and it is one of the strongest heat-treatable aluminium alloys. It offers excellent strength-to-weight ratio.

Surface Finish:The surface finish of 2014 aluminium flat bar can vary based on manufacturing processes. It can be finished to achieve different levels of smoothness or roughness.

2014 Aluminium Flat Bars


Alloy : 2014 Aluminium Alloy


Temper: O H14 H18 / T351 T3 T4 / H24 H26 H16 / H32 H111 H321 H116 H112 / T6 T651 / T7451 T6511


Diameter: 10mm-500mm


Length: 500mm-6000mm


Standard: GB/T 3880-2012 ASTMB209 EN485


Surface Treatment: Mill Finish / Brush PSolish / Bright Finish


MOQ: The inventory has no MOQ 2mt-3mt


Packing: Standard Export Packing


Port of Dispatch: It depends on the supplier's location and shipping arrangements


Delivery Time: The inventory is 5-7 days . 25-30 days for customized products


Payment: TT / LC / TT+LC


Applications:
Aerospace components | Aircraft structures | Automotive parts | Precision parts and components | Structural components requiring high strength

Chemical Composition

Aluminium (Al): 90.7-94.7%
Copper (Cu): 3.9-5.0%
Iron (Fe): 0.50%
Silicon (Si): 0.50-1.2%
Manganese (Mn): 1.2-1.8%
Magnesium (Mg): 1.2-1.8%
Zinc (Zn): 1.2-1.8%
Titanium (Ti): 0.20-0.8%
Other 0.05%(each) 0.15(total)

Formability:While it has good machinability, 2014 may have reduced formability compared to some other aluminium alloys. It is essential to consider the forming requirements for the intended application.