3004 Aluminium Flat Bar
3004 aluminium flat bars can vary based on the manufacturer and customer requirements. Using 3004 aluminium for a specific application, it's advisable to consult with the relevant standards and specifications to ensure the alloy's suitability for the intended use.
| Details and Characteristics: |
|---|
|
Welding: 3004 aluminium can be easily welded using conventional methods, making it suitable for fabrication processes. Formability: 3004 aluminium is known for its good formability, making it suitable for various forming and shaping processes. It can be easily formed, welded, and brazed. Surface Finish: The surface finish of 3004 aluminium flat bar can vary based on manufacturing processes. It can be finished to achieve different levels of smoothness or roughness. Corrosion Resistance: This alloy exhibits good corrosion resistance, particularly in moist or corrosive environments. It is often used in applications where resistance to atmospheric corrosion is essential. |
3004 Aluminium Flat Bars
Alloy: 3004 Aluminium Alloy
Temper:
O H14 H18 / T351 T3 T4 / H24 H26 H16 / H32 H111 H321 H116 H112 / T6 T651 / T7451 T6511
Diameter: 10mm-500mm
Length: 500mm-6000mm
Standard: GB/T 3880-2012 ASTMB209 EN485
Surface Treatment: Mill Finish / Brush PSolish / Bright Finish
MOQ: The inventory has no MOQ 2mt-3mt
Packing: Standard Export Packing
Port of Dispatch: It depends on the supplier's location and shipping arrangements
Delivery Time: The inventory is 5-7 days . 25-30 days for customized products
Payment: TT / LC / TT+LC
Applications:
Beverage cans and lids | Roofing and siding materials | Cooking utensils | Chemical and food processing equipment | Heat exchangers
Chemical Composition |
|
| Aluminium (Al): | 95.7% |
|---|---|
| Copper (Cu): | 0.25% |
| Iron (Fe): | 0.7% |
| Manganese (Mn): | 1.0-1.5% |
| Magnesium (Mg): | 0.8-1.3% |
| Silicon (Si): | 0.3% |
| Zinc (Zn): | 0.25% |
| Other | 0.05%(each) 0.15(total) |
Non-Heat Treatable: 3004 is a non-heat treatable aluminium alloy, meaning it doesn't undergo any strengthening through heat treatment processes. Its properties are primarily determined by cold working or strain hardening.