2014 Aluminium Hex Bar
2014 aluminum hex bars can vary based on the manufacturer and customer requirements. Using 2014 aluminum for a specific application, it's advisable to consult with the relevant standards and specifications to ensure the alloy's suitability for the intended use.
| Details and Characteristics: |
|---|
High Strength: 2014 is known for its high strength and excellent heat resistance. It is one of the strongest aluminum alloys. Good Machinability: This alloy offers good machinability, making it suitable for various machining and fabrication processes. Corrosion Resistance: 2014 has moderate corrosion resistance. Its use is often limited to applications where corrosion is not a significant concern. Heat Treatment: 2014 is heat-treatable and can be strengthened through various heat treatment processes, such as solution heat treatment and precipitation hardening. Applications: Aerospace components, Aircraft structures and Fuselage frames | High-stress structural parts | Automotive components | Defense and military applications | Machinery and equipment parts |
2014 Aluminium Hex Bars
Alloy : 2014 Aluminium Alloy
Temper:
O H14 H18 / T351 T3 T4 / H24 H26 H16 / H32 H111 H321 H116 H112 / T6 T651 / T7451 T6511
Diameter: 10mm-500mm
Length: 500mm-6000mm
Standard: GB/T 3880-2012 ASTMB209 EN485
Surface Treatment: Mill Finish / Brush PSolish / Bright Finish
MOQ: The inventory has no MOQ 2mt-3mt
Packing: Standard Export Packing
Port of Dispatch: It depends on the supplier's location and shipping arrangements
Delivery Time: The inventory is 5-7 days . 25-30 days for customized products
Payment: TT / LC / TT+LC
Chemical Composition |
|
| Aluminum (Al): | 90.7% |
|---|---|
| Copper (Cu): | 3.9-5.0% |
| Iron (Fe): | 0.50% max |
| Silicon (Si): | 0.50-1.2% |
| Manganese (Mn): | 1.2-1.8% |
| Magnesium (Mg): | 1.2-1.8% |
| Zinc (Zn): | 0.25% max |
| Titanium (Ti): | 0.20% max |
| Other elements: | 0.15% each, 0.75% total |
Weldability: While 2014 aluminum is generally not recommended for welding due to its high copper content, it can be welded using certain techniques. However, welding is usually avoided in critical applications.
Surface Finish: The surface finish of 2014 aluminum hex bars can vary based on manufacturing processes. It can be finished to achieve different levels of smoothness or roughness.