Aluminium alloy 6082 is a high-strength, heat-treatable alloy known for its excellent corrosion resistance, machinability, and weldability. It belongs to the 6xxx series and is primarily composed of magnesium and silicon as its principal alloying elements, with additional elements to enhance specific properties.
| Properties of 6082 Aluminium Alloy |
|---|
Formability: The alloy has good formability, allowing for the production of intricate shapes and designs. This property is advantageous for the extrusion of pipes and tubes with specific profiles. Heat Treatability: 6082 alloy is heat-treatable, allowing for the enhancement of mechanical properties through various heat treatment processes, such as solution heat treatment and artificial aging. Good Weldability: 6082 aluminum alloy is easily weldable using various techniques, including MIG and TIG welding. This property is essential for the fabrication of components, including pipes and tubes. Versatility in Extrusion: The versatility of 6082 alloy in the extrusion process allows for the production of pipes and tubes with a wide range of dimensions and profiles, meeting diverse application requirements. Anodizing Capability: 6082 alloy can be effectively anodized, providing additional corrosion resistance and allowing for a wide range of decorative finishes. This is beneficial for applications in architecture and design. Excellent Corrosion Resistance: The alloy exhibits excellent corrosion resistance, particularly in environments with exposure to moisture and other corrosive elements. This corrosion resistance makes it suitable for outdoor applications. Machinability: The alloy offers good machinability, allowing for efficient machining processes. This is particularly important in applications where precise machining is required, such as in the production of components for pipes and tubes. High Strength: 6082 alloy is known for its high strength, making it suitable for applications where structural integrity and load-bearing capabilities are essential. The alloy achieves its strength through a combination of solid solution strengthening and precipitation hardening. |
Alloy : 6082 Aluminium Alloy
Temper:
O / F / T3, T4, T5, T6, T7, T351, T451, T651, T851 / H12, H14, H16, H18, H19, H22, H24, H26, H32, H34, H36, H38, H111, H112, H321
Wall Thickness:01mm to 400mm
Type of Pipe: Seamless pipe /Seam pipe /Weld pipe
Standard: GB/T 3880-2012 ASTMB209 EN485
Surface Treatment: Mill Finish / Brush Polish / Bright Finish
MOQ: The inventory has no MOQ 2mt-3mt
Packing: Standard Export Packing
Port of Dispatch: It depends on the supplier's location and shipping arrangements
Delivery Time: The inventory is 5-7 days . 25-30 days for customized products
Payment: TT / LC / TT+LC
Chemical Composition |
|
| Aluminium (Al): | 97.4% |
|---|---|
| Silicon (Si): | 0.7-1.3% |
| Iron (Fe): | 0.5% |
| Manganese (Mn): | 0.4-1.0% |
| Magnesium (Mg): | 1.0-1.8% |
| Chromium (Cr): | 0.25-1.2% |
| Zinc (Zn): | 0.2% |
| Titanium (Ti): | 0.1% |
| Copper (Cu): | 0.1% |
| Other Elements: | 0.05% (each), 0.15%(total) |