Aluminum alloy 1050 is a commercially pure aluminum alloy with excellent formability, corrosion resistance, and electrical conductivity. However, it is not heat-treatable. Aluminum round bars made from 1050 alloy are commonly used in various applications.
| Properties: |
|---|
|
Density:2.7 g/cm³ Melting Point:640°C (1184°F) Tensile Strength:55 MPa (8,000 psi) Yield Strength:45 MPa (6,500 psi) Elongation at Break:27% Modulus of Elasticity:70 GPa (10,000 ksi) |
| Details and Characteristics: |
|
Formability: 1050 aluminum has excellent formability and is often used in applications that require intricate forming and bending. Corrosion Resistance: It offers good corrosion resistance in mild environments, but it is not as corrosion-resistant as some other aluminum alloys. Electrical Conductivity: 1050 aluminum has high electrical conductivity, making it suitable for electrical applications. Weldability: It has good weldability using conventional welding methods, although special precautions may be needed to avoid cracking. Applications: Commonly used in applications where formability and electrical conductivity are crucial, such as electrical conductors, reflectors, nameplates, and various decorative uses. Surface Finish: 1050 aluminum is often used in applications where a bright, reflective surface finish is desirable. |
Alloy: 1050 Aluminium Alloy
Temper:
O H14 H18 / T351 T3 T4 / H24 H26 H16 / H32 H111 H321 H116 H112 / T6 T651 / T7451 T6511
Diameter: 10mm-500mm
Length: 500mm-6000mm
Standard: GB/T 3880-2012 ASTMB209 EN485
Surface Treatment: Mill Finish / Brush PSolish / Bright Finish
MOQ: The inventory has no MOQ 2mt-3mt
Packing: Standard Export Packing
Port of Dispatch: It depends on the supplier's location and shipping arrangements
Delivery Time: The inventory is 5-7 days . 25-30 days for customized products
Payment: TT / LC / TT+LC
Chemical Composition |
|
| Aluminium (Al): | 99.5% |
|---|---|
| Iron (Fe): | 0.4% |
| Copper (Cu): | 0.05% |
| Manganese (Mn): | 0.05% |
| Zinc (Zn): | 0.05% |