2017 Aluminium Round Bar
Aluminum alloy 2017 is a high-strength aluminum alloy with excellent machinability. It belongs to the 2000 series of aluminum alloys and is often used in aerospace and military applications.
| Properties: |
|---|
|
Density: 2.78 g/cm³ Melting Point: Approximately 540°C (1004°F) Tensile Strength: Varies based on temper and processing. Yield Strength: Varies based on temper and processing. Elongation at Break: Varies based on temper and processing. Modulus of Elasticity: Approximately 70 GPa (10,200 ksi) Machinability: Excellent |
| Details and Characteristics: |
|
Machinability: 2017 aluminum alloy is known for its excellent machinability, making it suitable for applications where intricate and high-speed machining is required. High Strength: It has high strength, particularly when compared to other aluminum alloys with similar machinability. Weldability: It has fair weldability, but preheating is often required to avoid cracking during welding. Corrosion Resistance: While it offers reasonable corrosion resistance, it is not as corrosion-resistant as some other aluminum alloys. Heat Treatability: 2017 aluminum can be heat-treated to achieve various temper conditions, impacting its mechanical properties. Applications: Commonly used in aerospace and military applications, including aircraft components and structural parts, where both strength and machinability are crucial. Surface Finish: 2017 aluminum is often used in applications where a smooth surface finish is desirable. |
2017 Aluminium Round Bars
Alloy : 2017 Aluminium Alloy
Temper:
O H14 H18 / T351 T3 T4 / H24 H26 H16 / H32 H111 H321 H116 H112 / T6 T651 / T7451 T6511
Diameter: 10mm-500mm
Length: 500mm-6000mm
Standard: GB/T 3880-2012 ASTMB209 EN485
Surface Treatment: Mill Finish / Brush PSolish / Bright Finish
MOQ: The inventory has no MOQ 2mt-3mt
Packing: Standard Export Packing
Port of Dispatch: It depends on the supplier's location and shipping arrangements
Delivery Time: The inventory is 5-7 days . 25-30 days for customized products
Payment: TT / LC / TT+LC
Chemical Composition |
|
| Aluminum (Al): | 91.7% |
|---|---|
| Copper (Cu): | 3.5% - 4.5% |
| Manganese (Mn): | 1.2% - 2.0% |
| Iron (Fe): | 0.7% |
| Silicon (Si): | 0.7% |
| Zinc (Zn): | 0.7% - 1.3% |
| Nickel (Ni): | 0.1% |
| Other | 0.05%(each) 0.15(total) |