Aluminum alloy 2011 is a high-strength aluminum alloy with excellent machinability. It belongs to the 2000 series of aluminum alloys and is often used in applications where machining and high mechanical strength are crucial.
| Properties: |
|---|
Density: 2.78 g/cm3 Melting Point: Approximately 535oC (995oF) Tensile Strength: Varies based on temper and processing. Yield Strength: Varies based on temper and processing. Elongation at Break: Varies based on temper and processing. Modulus of Elasticity: Approximately 71 GPa (10,300 ksi) Machinability: Excellent |
| Details and Characteristics: |
Machinability: 2011 aluminum alloy is known for its excellent machinability, making it suitable for applications where intricate and high-speed machining is required. High Strength: It has good strength, especially when compared to other aluminum alloys with similar machinability. Free-Cutting Alloy: The addition of bismuth and lead makes it a free-cutting alloy, improving machinability. |
Alloy : 2011 Aluminium Alloy
Temper:
O H14 H18 / T351 T3 T4 / H24 H26 H16 / H32 H111 H321 H116 H112 / T6 T651 / T7451 T6511
Diameter: 10mm-500mm
Length: 500mm-6000mm
Standard: GB/T 3880-2012 ASTMB209 EN485
Surface Treatment: Mill Finish / Brush PSolish / Bright Finish
MOQ: The inventory has no MOQ 2mt-3mt
Packing: Standard Export Packing
Port of Dispatch: It depends on the supplier's location and shipping arrangements
Delivery Time: The inventory is 5-7 days . 25-30 days for customized products
Payment: TT / LC / TT+LC
Chemical Composition |
|
| Aluminum (Al): | 91.1% |
|---|---|
| Copper (Cu): | 6.0% - 7.0% |
| Bismuth (Bi): | 0.20% - 0.60% |
| Lead (Pb): | 0.20% - 0.60% |
| Iron (Fe): | 0.7% |
| Zinc (Zn): | 0.3% |
| Silicon (Si): | 0.4% - 0.8% |
| Manganese (Mn): | 0.4% - 1.0% |
| Other | 0.05%(each) 0.15(total) |