Aluminum alloy 2014 is a high-strength aluminum alloy with excellent machinability. It belongs to the 2000 series of aluminum alloys and is often used in aerospace applications and other high-stress environments.
| Properties: |
|---|
Density: 2.78 g/cm³ Melting Point: Approximately 640°C (1184°F) Tensile Strength: Varies based on temper and processing. Yield Strength: Varies based on temper and processing. Elongation at Break: Varies based on temper and processing. Modulus of Elasticity: Approximately 72 GPa (10,400 ksi) Machinability: Excellent |
| Details and Characteristics: |
Weldability: It has fair weldability, but preheating is often required to avoid cracking during welding. High Strength: It has high strength, particularly when compared to other aluminum alloys with similar machinability. Heat Treatability: 2014 aluminum can be heat-treated to achieve various temper conditions, impacting its mechanical properties. |
Alloy : 2014 Aluminium Alloy
Temper:
O H14 H18 / T351 T3 T4 / H24 H26 H16 / H32 H111 H321 H116 H112 / T6 T651 / T7451 T6511
Diameter: 10mm-500mm
Length: 500mm-6000mm
Standard: GB/T 3880-2012 ASTMB209 EN485
Surface Treatment: Mill Finish / Brush PSolish / Bright Finish
MOQ: The inventory has no MOQ 2mt-3mt
Packing: Standard Export Packing
Port of Dispatch: It depends on the supplier's location and shipping arrangements
Delivery Time: The inventory is 5-7 days . 25-30 days for customized products
Payment: TT / LC / TT+LC
Chemical Composition |
|
| Aluminum (Al): | 90.7% |
|---|---|
| Copper (Cu): | 3.9% - 5.0% |
| Manganese (Mn): | 1.2% - 1.8% |
| Iron (Fe): | 0.7% |
| Silicon (Si): | 0.50% |
| Zinc (Zn): | 1.2% - 1.8% |
| Nickel (Ni): | 0.1% |
| Other | 0.05%(each) 0.15(total) |