Aluminum alloy 5356 is a non-heat-treatable alloy known for its good weldability and corrosion resistance. It belongs to the 5000 series of aluminum alloys and is commonly used as a welding filler material.
| Properties: |
|---|
|
Density: 2.69 g/cm3 Melting Point: Approximately 575oC (1067oF) Tensile Strength: Varies based on temper and processing. Yield Strength: Varies based on temper and processing. Elongation at Break: Varies based on temper and processing. Modulus of Elasticity: Approximately 72 GPa (10,500 ksi) Corrosion Resistance: Good |
| Details and Characteristics: |
Formability: It has good formability, allowing it to be shaped and bent for various applications. Surface Finish: 5356 aluminum is often used in applications where a smooth, reflective surface finish is desirable. Heat Treatment: 5356 is not typically subjected to heat treatment, as its strength is primarily derived from solid solution strengthening. |
Alloy : 5356 Aluminium Alloy
Temper:
O H14 H18 / T351 T3 T4 / H24 H26 H16 / H32 H111 H321 H116 H112 / T6 T651 / T7451 T6511
Diameter: 10mm-500mm
Length: 500mm-6000mm
Standard: GB/T 3880-2012 ASTMB209 EN485
Surface Treatment: Mill Finish / Brush PSolish / Bright Finish
MOQ: The inventory has no MOQ 2mt-3mt
Packing: Standard Export Packing
Port of Dispatch: It depends on the supplier's location and shipping arrangements
Delivery Time: The inventory is 5-7 days . 25-30 days for customized products
Payment: TT / LC / TT+LC
Chemical Composition |
|
| Aluminum (Al): | 98.9% |
|---|---|
| Copper (Cu): | 0.1% |
| Iron (Fe): | 0.4% |
| Manganese (Mn): | 0.05% - 0.2% |
| Magnesium (Mg): | 4.5% - 5.5% |
| Chromium (Cr): | 0.05% - 0.2% |
| Zinc (Zn): | 0.1% |
| Other | 0.05%(each) 0.15(total) |