2014 Aluminium Plate
Aluminum alloy 2014 is a high-strength, heat-treatable aluminum alloy that belongs to the 2000 series. It is known for its excellent machinability and good mechanical properties.
| Properties: |
|---|
Density: 2.78 g/cm3 Melting Point: 640oC (1184oF) Tensile Strength: 483 MPa (70,000 psi) Yield Strength: 448 MPa (65,000 psi) Elongation at Break: 11% Modulus of Elasticity: 73.1 GPa (10,600 ksi) Thermal Conductivity: 163 W/m.K |
| Details and Characteristics: |
High Strength:2014 alloy offers high strength, particularly in comparison to other aluminum alloys. Heat-Treatable:It is a heat-treatable alloy, allowing for the improvement of mechanical properties through heat treatment processes. Machinability:While not as good as the 2000 series alloy 2011 in terms of machinability, 2014 aluminum still exhibits good machinability. Limited Corrosion Resistance:It provides reasonable corrosion resistance but is not as corrosion-resistant as some other aluminum alloys. |
2014 Aluminium Plates
Alloy : 2014 Aluminium Alloy
Temper :
O H14 H24 H18 / T351 T3 T4 T651 T6 / H14 H24 H26 H16 / H32 H111 H321 H116 H112 / T6 T651 / T651 T6 T7451
Thickness : 0.2mm-300mm
Width : 500mm-3000mm
Standard : GB/ 3880-2012 ASTMB209 EN485
Surface Treatment : Mill finish / Brush polish
PVC Coated : One side or two side PVC
MOQ : The inventory has no MOQ
Packing : Standard Export Packing
Port of Dispatch : It depends on the supplier's location and shipping arrangements
Delivery Time : The inventory is 5-7 days . 25-30 days for customized products
Payment : TT / LC / TT+LC
Chemical Composition |
|
| Aluminium (Al): | 90.7% |
|---|---|
| Copper (Cu): | 4.4% |
| Iron (Fe): | 1.3% |
| Manganese (Mn): | 1.2% - 1.8% |
| Magnesium (Mg):: | 1.2% - 1.8% |
| Nickel (Ni): | 0.2% - 0.8% |
| Zinc (Zn): | 3.9% - 5.0% |
| Others: | 0.5%(each) 0.15%(total) |
Applications:
Commonly used in aerospace applications, including aircraft structures and other high-stress applications. It is also used in various industrial applications where a combination of strength and machinability is required.