Aluminum alloy 3003 is a non-heat-treatable, corrosion-resistant alloy that belongs to the 3000 series of aluminum alloys. It is widely used for various applications due to its excellent forming and welding characteristics, good corrosion resistance, and moderate strength.
| Properties: |
|---|
Density:2.73 g/cm³ Melting Point:655°C (1215°F) Tensile Strength:130 MPa (18,900 psi) Yield Strength:115 MPa (16,700 psi) Elongation at Break:20% Modulus of Elasticity:69 GPa (10,000 ksi) Thermal Conductivity:163 W/m·K Electrical Conductivity:31% IACS (International Annealed Copper Standard) |
| Details and Characteristics: |
Weldability: It has good weldability, allowing for various welding and joining methods. Excellent Formability: 3003 alloy is known for its excellent formability, making it suitable for a wide range of forming processes. Moderate Strength: While not as strong as some other aluminum alloys, 3003 alloy still offers sufficient strength for many applications. |
Alloy : 3003 Aluminium Alloy
Temper :
O H14 H24 H18 / T351 T3 T4 T651 T6 / H14 H24 H26 H16 / H32 H111 H321 H116 H112 / T6 T651 / T651 T6 T7451
Thickness : 0.2mm-300mm
Width : 500mm-3000mm
Standard : GB/ 3880-2012 ASTMB209 EN485
Surface Treatment : Mill finish / Brush polish
PVC Coated : One side or two side PVC
MOQ : The inventory has no MOQ
Packing : Standard Export Packing
Port of Dispatch : It depends on the supplier's location and shipping arrangements
Delivery Time : The inventory is 5-7 days . 25-30 days for customized products
Payment : TT / LC / TT+LC
Chemical Composition |
|
| Aluminium (Al): | 98.6% |
|---|---|
| Copper (Cu): | 0.05% - 0.20% |
| Iron (Fe): | 0.70% |
| Manganese (Mn): | 1.0% - 1.5% |
| Zinc (Zn): | 0.10% |