Aluminum alloy 3105 is a non-heat-treatable wrought alloy primarily composed of aluminum, manganese, and a small amount of magnesium. It belongs to the 3000 series of aluminum alloys and is known for its good corrosion resistance, formability, and weldability.
| Properties: |
|---|
|
Density:2.73 g/cm³ Melting Point:615°C (1139°F) Tensile Strength:172 MPa (25,000 psi) Yield Strength:138 MPa (20,000 psi) Elongation at Break:12% Modulus of Elasticity:69 GPa (10,000 ksi) Thermal Conductivity:195 W/m·K |
| Details and Characteristics: |
Weldability:It has good weldability, allowing for various welding and joining methods. Paintability:3105 alloy is suitable for painting, and it is often coated for additional protection and aesthetics. Good Formability:3105 alloy is known for its good formability, making it suitable for a variety of forming processes. Corrosion Resistance:3105 aluminum provides good corrosion resistance, particularly in outdoor environments. It is often used in architectural applications. |
Alloy: 3105 Aluminium Alloy
Temper:
O H14 H24 H18 / T351 T3 T4 T651 T6 / H14 H24 H26 H16 / H32 H111 H321 H116 H112 / T6 T651 / T651 T6 T7451
Thickness: 0.2mm-300mm
Width: 500mm-3000mm
Standard: GB/ 3880-2012 ASTMB209 EN485
Surface Treatment: Mill finish / Brush polish
PVC Coated: One side or two side PVC
MOQ: The inventory has no MOQ
Packing: Standard Export Packing
Port of Dispatch: It depends on the supplier's location and shipping arrangements
Delivery Time: The inventory is 5-7 days . 25-30 days for customized products
Payment: TT / LC / TT+LC
Chemical Composition |
|
| Aluminium (Al): | 99.0% |
|---|---|
| Copper (Cu): | 0.30% |
| Iron (Fe): | 0.70% |
| Manganese (Mn): | 0.30% - 0.80% |
| Magnesium (Mg): | 0.20% |
| Zinc (Zn): | 0.25% |