Aluminum alloy 6082 is a medium-strength heat-treatable alloy that belongs to the 6000 series of aluminum alloys. It is similar to alloy 6061 but with slightly higher mechanical properties.
| Properties: |
|---|
|
Density: 2.70 g/cm³ Melting Point: 555°C (1031°F) Tensile Strength: Varies based on temper and thickness. Yield Strength: Varies based on temper and thickness. Elongation at Break: Varies based on temper and thickness. Modulus of Elasticity: Approximately 70 GPa (10,200 ksi) Thermal Conductivity: 180 W/m·K |
| Details and Characteristics: |
Weldability: 6082 aluminum has good weldability, allowing for various welding and joining methods. Strength-to-Weight Ratio: 6082 alloy provides a high strength-to-weight ratio, making it suitable for structural applications. Applications: Used in various applications, including structural components, architectural extrusions, and transportation equipment. Machinability: It has good machinability, making it suitable for various machining operations, including milling, drilling, and turning. |
Alloy: 6082 Aluminium Alloy
Temper:
O H14 H24 H18 / T351 T3 T4 T651 T6 / H14 H24 H26 H16 / H32 H111 H321 H116 H112 / T6 T651 / T651 T6 T7451
Thickness: 0.2mm-300mm
Width: 500mm-3000mm
Standard: GB/ 3880-2012 ASTMB209 EN485
Surface Treatment: Mill finish / Brush polish
PVC Coated: One side or two side PVC
MOQ: The inventory has no MOQ
Packing: Standard Export Packing
Port of Dispatch: It depends on the supplier's location and shipping arrangements
Delivery Time: The inventory is 5-7 days . 25-30 days for customized products
Payment: TT / LC / TT+LC
Chemical Composition |
|
| Aluminium (Al): | 97.4% |
|---|---|
| Iron (Fe): | 0.50% |
| Silicon (Si): | 0.70% - 1.30% |
| Copper (Cu): | 0.10% |
| Titanium (Ti): | 0.10% |
| Manganese (Mn): | 0.40% - 1.00% |
| Magnesium (Mg): | 1.00% - 1.80% |
| Zinc (Zn): | 0.20% |
| Chromium (Cr): | 0.25% - 1.20% |
| other | 0.05%(each) 0.15(total) |