2017 Aluminium Plate
Aluminum alloy 2017 is a high-strength, heat-treatable aluminum alloy known for its excellent machinability. It belongs to the 2000 series of aluminum alloys and is commonly used in aerospace and structural applications.
| Properties: |
|---|
Density: 2.78 g/cm³ Melting Point: 540°C (1004°F) Tensile Strength: 379 MPa (55,000 psi) Yield Strength: 221 MPa (32,000 psi) Elongation at Break: 12% Modulus of Elasticity: 71 GPa (10,300 ksi) Thermal Conductivity: 193 W/m·K |
| Details and Characteristics: |
High Strength: 2017 alloy offers high strength, making it suitable for applications where strength is a critical factor. Heat-Treatable: It is a heat-treatable alloy, allowing for the improvement of mechanical properties through heat treatment processes. Limited Corrosion Resistance: While it provides reasonable corrosion resistance, it is not as corrosion-resistant as some other aluminum alloys. |
2017 Aluminium Plates
Alloy : 2017 Aluminium Alloy
Temper :
O H14 H24 H18 / T351 T3 T4 T651 T6 / H14 H24 H26 H16 / H32 H111 H321 H116 H112 / T6 T651 / T651 T6 T7451
Thickness : 0.2mm-300mm
Width : 500mm-3000mm
Standard : GB/ 3880-2012 ASTMB209 EN485
Surface Treatment : Mill finish / Brush polish
PVC Coated : One side or two side PVC
MOQ : The inventory has no MOQ
Packing : Standard Export Packing
Port of Dispatch : It depends on the supplier's location and shipping arrangements
Delivery Time : The inventory is 5-7 days . 25-30 days for customized products
Payment : TT / LC / TT+LC
Chemical Composition |
|
| Aluminium (Al): | 90.70% |
| Copper (Cu): | 3.5% - 4.5% |
| Iron (Fe): | 0.70% |
| Manganese (Mn): | 1.4% - 2.0% |
| Magnesium (Mg):: | 1.5% - 2.3% |
| Zinc (Zn): | 0.20% - 0.60% |
| Chromium (Cr): | 0.10% - 0.25% |
| Others: | 0.5%(each) 0.15%(total) |
Good Machinability: 2017 aluminum is known for its excellent machinability, making it suitable for applications where intricate machining is required.
Applications: Commonly used in aerospace applications, including aircraft structures and components. It is also utilized in high-strength applications such as marine components and structural parts.