Aluminum alloy 3004 is a non-heat-treatable, moderate-strength alloy that belongs to the 3000 series of aluminum alloys. It is widely used for various applications due to its good formability, corrosion resistance, and weldability.
| Properties: |
|---|
Density:2.78 g/cm³ Melting Point:655°C (1215°F) Tensile Strength:276 MPa (40,000 psi) Yield Strength:240 MPa (35,000 psi) Elongation at Break:12% Modulus of Elasticity:70 GPa (10,200 ksi) Thermal Conductivity:167 W/m·K Electrical Conductivity:29% IACS (International Annealed Copper Standard) |
| Details and Characteristics: |
Weldability:It has good weldability, allowing for various welding and joining methods. Good Formability:3004 alloy is known for its good formability, making it suitable for a variety of forming processes. Moderate Strength:It offers moderate strength, making it suitable for applications where strength requirements are not as demanding. |
Alloy: 3004 Aluminium Alloy
Temper:
O H14 H24 H18 / T351 T3 T4 T651 T6 / H14 H24 H26 H16 / H32 H111 H321 H116 H112 / T6 T651 / T651 T6 T7451
Thickness: 0.2mm-300mm
Width: 500mm-3000mm
Standard: GB/ 3880-2012 ASTMB209 EN485
Surface Treatment: Mill finish / Brush polish
PVC Coated: One side or two side PVC
MOQ: The inventory has no MOQ
Packing: Standard Export Packing
Port of Dispatch: It depends on the supplier's location and shipping arrangements
Delivery Time: The inventory is 5-7 days . 25-30 days for customized products
Payment: TT / LC / TT+LC
Chemical Composition |
|
| Aluminium (Al): | 95.7% |
|---|---|
| Copper (Cu): | 0.25% |
| Iron (Fe): | 0.7% |
| Manganese (Mn): | 1.0% - 1.5% |
| Magnesium (Mg): | 0.8% - 1.3% |
| Zinc (Zn): | 0.25% |