Aluminum alloy 2017 is a high-strength, heat-treatable alloy with excellent machinability. It is often used in aerospace applications, as well as in various structural components.
Mechanical Properties: |
---|
Tensile Strength:52,000 psi (359 MPa) Yield Strength:40,000 psi (276 MPa) Elongation:15% |
Physical Properties: |
Density: 2.78 g/cm³ (0.100 lb/in³) Melting Range: 500°C-640°C (932°F-1184°F) |
Typical Uses: |
Aerospace components | Aircraft structures | Fasteners | Structural components | High-stress applications |
Welding: |
2017 is generally considered weldable using standard methods, although welding should be approached with caution due to its high copper content. Processes like gas tungsten arc welding (GTAW/TIG) or gas metal arc welding (GMAW/MIG) are commonly used. |
Corrosion Resistance: |
2017 has moderate corrosion resistance. It is not as corrosion-resistant as some other aluminum alloys, but it is suitable for many applications. Its primary use is in situations where high strength and machinability are required. |
Alloy: 2017 Aluminium Sheet
Temper:
O H14 H24 H18 / T351 T3 T4 T651 T6 / H14 H24 H26 H16 / H32 H111 H321 H116 H112 / T6 T651 / T651 T6 T7451
T4: Solution heat-treated and naturally aged to a substantially stable condition.
T451: Solution heat-treated, stress-relieved by stretching, and artificially aged.
T6: Solution heat-treated and artificially aged.
Thickness: 0.2mm-300mm
Width: 500mm-3000mm
Standard: GB/ 3880-2012 ASTMB209 EN485
Surface Treatment: Mill finish / Brush polish
PVC Coated: One side or two side PVC
MOQ: The inventory has no MOQ
Packing: Standard Export Packing
Port of Dispatch: It depends on the supplier's location and shipping arrangements
Delivery Time: The inventory is 5-7 days . 25-30 days for customized products
Payment: TT / LC / TT+LC
Alloy 2017 Composition: |
|
Aluminum (Al): | 90.7% |
Silicon (Si): | 0.4% |
Iron (Fe): | 0.7% |
Copper (Cu): | 3.5%-4.5% |
Manganese (Mn): | 1.2%-2.0% |
Magnesium (Mg): | 1.5%-2.3% |
Titanium (Ti): | 0.2%-0.4% |
Zinc (Zn) | 0.7%-1.3% |
Others: | 0.15% (each), 0.15% (total) |