Aluminum alloy 5182 is a high-magnesium alloy that is commonly used in the manufacturing of beverage cans and automotive parts due to its combination of strength, formability, and corrosion resistance. Here are some details about 5182 aluminum alloy:
Mechanical Properties: |
---|
Tensile Strength: 32,000 psi (220 MPa) Yield Strength: 26,000 psi (180 MPa) Elongation: 13% |
Physical Properties: |
Density: 2.68 g/cm3 (0.0975 lb/in3) Melting Range: 580oC-640oC (1076oF-1184oF) |
Typical Uses: |
Beverage can ends and tabs | Automotive parts (e.g., body panels, fuel tanks) | Tin can lids | General sheet metal applications |
Welding: |
5182 is readily weldable using standard methods such as gas, electric, resistance, and spot welding. It is commonly used in applications where welding is required, such as in the automotive industry. |
Corrosion Resistance: |
5182 exhibits good corrosion resistance, making it suitable for applications in aggressive environments. However, its corrosion resistance is not as high as some other aluminum alloys like 5xxx series alloys. |
Alloy: 5182 Aluminium Alloy
Temper:
O H14 H24 H18 / T351 T3 T4 T651 T6 / H14 H24 H26 H16 / H32 H111 H321 H116 H112 / T6 T651 / T651 T6 T7451
H19: Strain-hardened, 1/2 hard. The highest strength in the 5182 series, suitable for can end stock.
H38: Strain-hardened, full hard. Maximum strength achieved through cold working.
Thickness: 0.2mm-300mm
Width: 500mm-3000mm
Standard: GB/ 3880-2012 ASTMB209 EN485
Surface Treatment: Mill finish / Brush polish
PVC Coated: One side or two side PVC
MOQ: The inventory has no MOQ
Packing: Standard Export Packing
Port of Dispatch: It depends on the supplier's location and shipping arrangements
Delivery Time: The inventory is 5-7 days . 25-30 days for customized products
Payment: TT / LC / TT+LC
Alloy 5182 Composition: |
|
Aluminum (Al): | 94.8% |
Magnesium (Mg): | 4.0%-5.0% |
Iron (Fe): | 0.35% |
Copper (Cu): | 0.1% |
Manganese (Mn): | 0.2%-0.5% |
Chromium (Cr): | 0.1% |
Others: | 0.05% (each) 0.15% (total) |