3003 Aluminium Sheets
Aluminum alloy 3003 is a non-heat-treatable alloy with excellent formability, corrosion resistance, and weldability. It is often used for applications that require moderate strength and good workability.
| Mechanical Properties: |
|---|
|
Tensile Strength:22,000 psi (152 MPa) Yield Strength:21,000 psi (145 MPa) Elongation:14% |
| Physical Properties: |
|
Density: 2.73 g/cm³ (0.098 lb/in³) Melting Range: 43°C-657°C (1190°F-1215°F) |
| Welding: |
| Alloy 3003 is readily weldable using standard methods such as gas, electric, resistance, and spot welding. |
| Corrosion Resistance: |
| 3003 has excellent corrosion resistance, particularly in atmospheric conditions. It is resistant to saltwater, making it suitable for coastal applications. |
| Considerations |
| 3003 is known for its good formability, making it suitable for applications that require shaping, bending, or drawing. It is commonly used in applications where moderate strength is sufficient. |
3003 Aluminium Sheets
Alloy: 3003 Aluminium Alloy
Temper:
O H14 H24 H18 / T351 T3 T4 T651 T6 / H14 H24 H26 H16 / H32 H111 H321 H116 H112 / T6 T651 / T651 T6 T7451
H12: Strain-hardened, 1/4 hard. Increased strength achieved by cold working and partial annealing.
H14: Strain-hardened, 1/2 hard. Higher strength and improved formability compared to H12.
H16: Strain-hardened, 3/4 hard. Increased strength with some retention of formability.
H18: Strain-hardened, full hard. Maximum strength achieved through cold working and annealing.
O: Fully annealed, soft condition with the lowest strength. Excellent workability for deep drawing or spinning.
Thickness: 0.2mm-300mm
Width: 500mm-3000mm
Standard: GB/ 3880-2012 ASTMB209 EN485
Surface Treatment: Mill finish / Brush polish
PVC Coated: One side or two side PVC
MOQ: The inventory has no MOQ
Packing: Standard Export Packing
Port of Dispatch: It depends on the supplier's location and shipping arrangements
Delivery Time: The inventory is 5-7 days . 25-30 days for customized products
Payment: TT / LC / TT+LC
Alloy 3003 Composition: |
|
| Aluminum (Al): | 98.6% |
| Silicon (Si): | 0.6% |
| Iron (Fe): | 0.7% |
| Copper (Cu): | 0.2% |
| Manganese (Mn): | 1.0%-1.5% |
| Zinc (Zn) | 0.1% |
| Others: | 0.05% (each), 0.15% (total) |