5086 Aluminium Sheet
Aluminum alloy 5086 is a high-strength, non-heat-treatable alloy with excellent corrosion resistance, especially in marine environments. Similar to 5083, it is often used in applications that require high strength and resistance to corrosive environments.
| Mechanical Properties: |
|---|
|
Tensile Strength: 42,000 psi (290 MPa) Yield Strength: 28,000 psi (193 MPa) Elongation: 12% |
| Physical Properties: |
|
Density: 2.66 g/cm³ (0.096 lb/in³) Melting Range: 570°C-640°C (1058°F-1184°F) |
| Welding: |
| 5086 is readily weldable using standard methods such as gas, electric, resistance, and spot welding. It has good weldability and performs well in post-weld heat treatment. |
| Corrosion Resistance: |
| 5086 exhibits excellent corrosion resistance, particularly in marine environments. It is known for its high resistance to stress corrosion cracking and general corrosion in aggressive conditions. |
| Considerations |
| 5086 is often chosen for its combination of high strength and corrosion resistance. Like 5083, it is not heat-treatable but gains strength through strain hardening. |
5086 Aluminium Sheets
Alloy: 5086 Aluminium Alloy
Temper:
O H14 H24 H18 / T351 T3 T4 T651 T6 / H14 H24 H26 H16 / H32 H111 H321 H116 H112 / T6 T651 / T651 T6 T7451
H116: Strain-hardened from a hot-worked condition, stabilized. The least amount of strain hardening with the highest ductility.
H321: Strain-hardened from a hot-worked condition, stabilized. Similar to H116 but with improved stress corrosion resistance.
O: Fully annealed, soft condition with the lowest strength. Excellent workability for deep drawing or spinning.
Thickness: 0.2mm-300mm
Width: 500mm-3000mm
Standard: GB/ 3880-2012 ASTMB209 EN485
Surface Treatment: Mill finish / Brush polish
PVC Coated: One side or two side PVC
MOQ: The inventory has no MOQ
Packing: Standard Export Packing
Port of Dispatch: It depends on the supplier's location and shipping arrangements
Delivery Time: The inventory is 5-7 days . 25-30 days for customized products
Payment: TT / LC / TT+LC
Alloy 5086 Composition: |
|
| Aluminum (Al): | 91.6% |
| Magnesium (Mg): | 3.5%-4.5% |
| Iron (Fe): | 0.0%-0.5% |
| Copper (Cu): | 0.1% |
| Manganese (Mn): | 0.2%-0.7% |
| Zinc (Zn) | 0.25% |
| Chromium (Cr): | 0.05%-0.25% |
| Titanium (Ti): | 0.15% |
| Others: | 0.05% (each) 0.15% (total) |
Typical Uses: Shipbuilding | Marine structures | Pressure vessels | LNG tankers | Welded structures | Tank trucks