1100 Aluminium Sheet
Aluminium alloy 1100 emerges as a standout choice in the realm of commercially pure aluminium alloys. With its composition predominantly comprising aluminium, typically hovering around 99%, this alloy boasts stellar corrosion resistance, positioning it as a prime candidate for applications exposed to moisture or corrosive environments.
| Mechanical Properties: |
|---|
| Tensile Strength: 13,000 psi (90 MPa) Yield Strength: 5,000 psi (35 MPa) Elongation: 30% |
| Physical Properties: |
| Density: 2.70 g/cm3 (0.0975 lb/in3) Melting Range: 643oC-657oC (1190oF-1215oF) |
| Typical Uses: |
|
Chemical and food processing equipment Heat exchangers Radiators General sheet metal work Refrigeration panels Cooking utensils |
| Welding: |
| Alloy 1100 is weldable by all standard methods, including gas, electric, resistance, and spot welding. |
| Corrosion Resistance: |
| Aluminum alloy 1100 has excellent corrosion resistance, particularly in atmospheric conditions. |
| Other Considerations: |
| Alloy 1100 is known for its high reflectivity, making it a popular choice for lighting fixtures, reflective materials, and decorative applications. |
1100 Aluminium Sheets
Alloy: 1100 Aluminium Alloy
Temper:
O H14 H24 H18 / T351 T3 T4 T651 T6 / H14 H24 H26 H16 / H32 H111 H321 H116 H112 / T6 T651 / T651 T6 T7451
O (Annealed):Fully annealed, soft condition with the lowest strength. It has excellent workability and is suitable for deep drawing or spinning.
H12: Strain-hardened, 1/4 hard. This temper is achieved by cold working and then partially annealing. It offers increased strength.
H14: Strain-hardened, 1/2 hard. Similar to H12 but with further cold working. It provides higher strength and improved formability.
H16: Strain-hardened, 3/4 hard. Achieved through cold working and further annealing. It offers increased strength but retains some formability.
H18: Strain-hardened, fully hard. This temper provides the highest strength but the lowest formability.
Thickness: 0.2mm-300mm
Width: 500mm-3000mm
Standard: GB/ 3880-2012 ASTMB209 EN485
Surface Treatment: Mill finish / Brush polish
PVC Coated: One side or two side PVC
MOQ: The inventory has no MOQ
Packing: Standard Export Packing
Port of Dispatch: It depends on the supplier's location and shipping arrangements
Delivery Time: The inventory is 5-7 days . 25-30 days for customized products
Payment: TT / LC / TT+LC
Alloy 1100 Composition: |
|
| Aluminum (Al): | 99.00% |
| Copper (Cu): | 0.05% |
| Iron (Fe): | 0.40% |
| Silicon (Si): | 0.95% |
| Manganese (Mn): | 0.05% |
| Zinc (Zn): | 0.10% |
| Titanium (Ti): | 0.10% |
| Other elements: | 0.05% each, 0.15% total |