5083 Aluminium Sheet
Aluminum alloy 5083 is a high-strength, non-heat-treatable alloy with excellent corrosion resistance, especially in marine environments. It is often used in applications that require high strength and resistance to corrosive environments.
| Mechanical Properties: |
|---|
|
Tensile Strength: 42,000 psi (290 MPa) Yield Strength: 21,000 psi (145 MPa) Elongation: 12% |
| Physical Properties: |
|
Density: (0.0975 lb/in³) Melting Range: 570°C-640°C (1058°F-1184°F) |
| Typical Uses: |
| Shipbuilding Marine structures Pressure vessels LNG tankers Armor plate Welded structures |
| Welding: |
| 5083 is readily weldable using standard methods such as gas, electric, resistance, and spot welding. It has good weldability with excellent performance in post-weld heat treatment. |
| Corrosion Resistance: |
| It is not heat-treatable but gains strength through strain hardening. |
| Considerations |
| 5083 has excellent corrosion resistance, particularly in seawater. It is known for its high resistance to stress corrosion cracking and general corrosion in marine environments. 5083 is known for its high strength and toughness, making it suitable for demanding applications in marine and aerospace industries. |
5083 Aluminium Sheets
Alloy : 1100 1050 1060 1070 1200 2011 2014 2017 2024 3003 3004 3005 3015 3105 5052 5083 5086 5154 5254 5356 5454 5056 5182 5754 6060 6061 6063 6082 6101 7020 7050 7075 8011 8090
Temper :
O H14 H24 H18 / T351 T3 T4 T651 T6 / H14 H24 H26 H16 / H32 H111 H321 H116 H112 / T6 T651 / T651 T6 T7451
H116: Strain-hardened from a hot-worked condition, stabilized. The least amount of strain hardening with the highest ductility.
H321: Strain-hardened from a hot-worked condition, stabilized. Similar to H116 but with improved stress corrosion resistance.
O: Fully annealed, soft condition with the lowest strength. Excellent workability for deep drawing or spinning.
Thickness : 0.2mm-300mm
Width : 500mm-3000mm
Standard : GB/ 3880-2012 ASTMB209 EN485
Surface Treatment : Mill finish / Brush polish
PVC Coated : One side or two side PVC
MOQ : The inventory has no MOQ
Packing : Standard Export Packing
Port of Dispatch : It depends on the supplier's location and shipping arrangements
Delivery Time : The inventory is 5-7 days . 25-30 days for customized products
Payment : TT / LC / TT+LC
Alloy 5083 Composition: |
|
| Aluminum (Al): | 91.9% |
| Magnesium (Mg): | 4.0%-4.9% |
| Iron (Fe): | 0.0%-0.4% |
| Copper (Cu): | 0.1% |
| Manganese (Mn): | 0.4%-1.0% |
| Zinc (Zn) | 0.25% |
| Chromium (Cr): | 0.05%-0.25% |
| Titanium (Ti): | 0.15% |
| Others: | 0.05% (each) 0.15% (total) |