3004 Aluminium Sheet
Aluminum alloy 3004 is a non-heat-treatable alloy with good formability, moderate strength, and excellent corrosion resistance. It is commonly used in applications where these properties are crucial.
| Mechanical Properties: |
|---|
|
Tensile Strength:31,000 psi (214 MPa) Yield Strength:21,000 psi (145 MPa) Elongation:20% |
| Physical Properties: |
|
Density: 2.78 g/cm3 (0.100 lb/in3) Melting Range: 643oC-657oC (1190oF-1215oF) |
| Typical Uses: |
| Beverage can bodies and ends Cooking utensils Food and chemical handling equipment Roofing and siding materials General sheet metal work |
| Welding: |
| Alloy 3004 is readily weldable using standard methods such as gas, electric, resistance, and spot welding. |
| Corrosion Resistance: |
| 3004 has excellent corrosion resistance, particularly in atmospheric conditions. It is also resistant to saltwater, making it suitable for coastal applications. |
| Considerations |
| 3004 is known for its good formability and weldability, making it suitable for applications that require shaping, bending, or joining through welding. It is commonly used in applications where moderate strength and corrosion resistance are essential. |
3004 Aluminium Sheets
Alloy: 3004 Aluminium Alloy
Temper:
O H14 H24 H18 / T351 T3 T4 T651 T6 / H14 H24 H26 H16 / H32 H111 H321 H116 H112 / T6 T651 / T651 T6 T7451
H12: Strain-hardened, 1/4 hard. Increased strength achieved by cold working and partial annealing.
H14: Strain-hardened, 1/2 hard. Higher strength and improved formability compared to H12.
H16: Strain-hardened, 3/4 hard. Increased strength with some retention of formability.
H18: Strain-hardened, full hard. Maximum strength achieved through cold working and annealing.
O: Fully annealed, soft condition with the lowest strength. Excellent workability for deep drawing or spinning.
Thickness: 0.2mm-300mm
Width: 500mm-3000mm
Standard: GB/ 3880-2012 ASTMB209 EN485
Surface Treatment: Mill finish / Brush polish
PVC Coated: One side or two side PVC
MOQ: The inventory has no MOQ
Packing: Standard Export Packing
Port of Dispatch: It depends on the supplier's location and shipping arrangements
Delivery Time: The inventory is 5-7 days . 25-30 days for customized products
Payment: TT / LC / TT+LC
Alloy 3004 Composition: |
|
| Aluminum (Al): | 95.7%-98.2% |
| Silicon (Si): | 0.3% |
| Iron (Fe): | 0.7% maximum |
| Copper (Cu): | 0.25% |
| Manganese (Mn): | 1.0%-1.5% |
| Magnesium (Mg): | 0.8%-1.3% |
| Zinc (Zn): | 0.25% |
| Others: | 0.05% (each), 0.15% (total) |