2017 Aluminium Sheet
Aluminum alloy 2017 is a high-strength, heat-treatable alloy with excellent machinability. It is often used in aerospace applications, as well as in various structural components.
| Mechanical Properties: |
|---|
|
Tensile Strength:52,000 psi (359 MPa) Yield Strength:40,000 psi (276 MPa) Elongation:15% |
| Physical Properties: |
|
Density: 2.78 g/cm³ (0.100 lb/in³) Melting Range: 500°C-640°C (932°F-1184°F) |
| Typical Uses: |
| Aerospace components Aircraft structures Fasteners Structural components High-stress applications |
| Welding: |
| 2017 is generally considered weldable using standard methods, although welding should be approached with caution due to its high copper content. Processes like gas tungsten arc welding (GTAW/TIG) or gas metal arc welding (GMAW/MIG) are commonly used. |
| Corrosion Resistance: |
| 2017 has moderate corrosion resistance. It is not as corrosion-resistant as some other aluminum alloys, but it is suitable for many applications. Its primary use is in situations where high strength and machinability are required. |
| Considerations |
| 2017 is known for its excellent machinability, making it suitable for applications requiring intricate or precise machining. |
2017 Aluminium Sheets
Alloy : 1100 1050 1060 1070 1200 2011 2014 2017 2024 3003 3004 3005 3015 3105 5052 5083 5086 5154 5254 5356 5454 5056 5182 5754 6060 6061 6063 6082 6101 7020 7050 7075 8011 8090
Temper :
O H14 H24 H18 / T351 T3 T4 T651 T6 / H14 H24 H26 H16 / H32 H111 H321 H116 H112 / T6 T651 / T651 T6 T7451
T4: Solution heat-treated and naturally aged to a substantially stable condition.
T451: Solution heat-treated, stress-relieved by stretching, and artificially aged.
T6: Solution heat-treated and artificially aged.
Thickness : 0.2mm-300mm
Width : 500mm-3000mm
Standard : GB/ 3880-2012 ASTMB209 EN485
Surface Treatment : Mill finish / Brush polish
PVC Coated : One side or two side PVC
MOQ : The inventory has no MOQ
Packing : Standard Export Packing
Port of Dispatch : It depends on the supplier's location and shipping arrangements
Delivery Time : The inventory is 5-7 days . 25-30 days for customized products
Payment : TT / LC / TT+LC
Alloy 2017 Composition: |
|
| Aluminum (Al): | 90.7% |
| Silicon (Si): | 0.4% |
| Iron (Fe): | 0.7% |
| Copper (Cu): | 3.5%-4.5% |
| Manganese (Mn): | 1.2%-2.0% |
| Magnesium (Mg): | 1.5%-2.3% |
| Titanium (Ti): | 0.2%-0.4% |
| Zinc (Zn) | 0.7%-1.3% |
| Others: | 0.15% (each), 0.15% (total) |