3105 Aluminium Sheet
Aluminum alloy 3105 is a non-heat-treatable alloy with good corrosion resistance, moderate strength, and excellent formability. It is commonly used in various applications where these properties are essential.
| Mechanical Properties: |
|---|
|
Tensile Strength:31,000 psi (214 MPa) Yield Strength:22,000 psi (152 MPa) Elongation:25% |
| Physical Properties: |
|
Density: 2.73 g/cm3 (0.098 lb/in3) Melting Range: 643oC-657oC (1190oF-1215oF) |
| Typical Uses: |
| Roofing and siding materials Building panels Food and chemical handling equipment Cooking utensils General sheet metal work |
| Welding: |
| Alloy 3105 is readily weldable using standard methods such as gas, electric, resistance, and spot welding. |
| Corrosion Resistance: |
| 3105 has good corrosion resistance, particularly in atmospheric conditions. It is also resistant to saltwater, making it suitable for coastal applications. |
| Considerations |
| 3105 is known for its excellent formability, making it suitable for applications that require shaping, bending, or deep drawing. It is commonly used in applications where corrosion resistance and formability are essential. |
3105 Aluminium Sheets
Alloy : 1100 1050 1060 1070 1200 2011 2014 2017 2024 3003 3004 3005 3015 3105 5052 5083 5086 5154 5254 5356 5454 5056 5182 5754 6060 6061 6063 6082 6101 7020 7050 7075 8011 8090
Temper :
O H14 H24 H18 / T351 T3 T4 T651 T6 / H14 H24 H26 H16 / H32 H111 H321 H116 H112 / T6 T651 / T651 T6 T7451
H12: Strain-hardened, 1/4 hard. Increased strength achieved by cold working and partial annealing.
H14: Strain-hardened, 1/2 hard. Higher strength and improved formability compared to H12.
H16: Strain-hardened, 3/4 hard. Increased strength with some retention of formability.
H18: Strain-hardened, full hard. Maximum strength achieved through cold working and annealing.
O: Fully annealed, soft condition with the lowest strength. Excellent workability for deep drawing or spinning.
Thickness : 0.2mm-300mm
Width : 500mm-3000mm
Standard : GB/ 3880-2012 ASTMB209 EN485
Surface Treatment : Mill finish / Brush polish
PVC Coated : One side or two side PVC
MOQ : The inventory has no MOQ
Packing : Standard Export Packing
Port of Dispatch : It depends on the supplier's location and shipping arrangements
Delivery Time : The inventory is 5-7 days . 25-30 days for customized products
Payment : TT / LC / TT+LC
Alloy 3105 Composition: |
|
| Aluminum (Al): | 97.3%-98.8% |
| Iron (Fe): | 0.7% |
| Copper (Cu): | 0.2% |
| Manganese (Mn): | 0.3%-0.8% |
| Magnesium (Mg): | 0.2% |
| Titanium (Ti): | 0.1% |
| Zinc (Zn) | 0.25% |
| Others: | 0.05% (each), 0.15% (total) |