Aluminum alloy 1200 is a commercially pure aluminum with high thermal conductivity and excellent corrosion resistance. It is often used in applications where these properties are critical.
Mechanical Properties: |
---|
Tensile Strength:15,000 psi (103 MPa) Yield Strength: 6,000 psi (41 MPa) Elongation: 35% |
Physical Properties: |
Density: 2.71 g/cm³ (0.0979 lb/in³) Melting Range: 640°C-660°C (1184°F-1220°F) |
Typical Uses: |
Reflectors Heat exchangers Chemical and food handling equipment Lighting applications Radiators |
Welding: |
Alloy 1200 is generally considered weldable using standard methods such as gas, electric, resistance, and spot welding. |
Corrosion Resistance: |
1200 has excellent corrosion resistance, particularly in atmospheric conditions. However, it is not suitable for applications where high corrosion resistance is critical. |
Considerations |
Alloy 1200 is known for its high thermal conductivity, making it a preferred choice for applications that require efficient heat transfer. |
Alloy : 1100 1050 1060 1070 1200 2011 2014 2017 2024 3003 3004 3005 3015 3105 5052 5083 5086 5154 5254 5356 5454 5056 5182 5754 6060 6061 6063 6082 6101 7020 7050 7075 8011 8090
Temper :
O H14 H24 H18 / T351 T3 T4 T651 T6 / H14 H24 H26 H16 / H32 H111 H321 H116 H112 / T6 T651 / T651 T6 T7451
O : Fully annealed, soft condition with the lowest strength. Excellent workability for deep drawing or spinning.
Thickness : 0.2mm-300mm
Width : 500mm-3000mm
Standard : GB/ 3880-2012 ASTMB209 EN485
Surface Treatment : Mill finish / Brush polish
PVC Coated : One side or two side PVC
MOQ : The inventory has no MOQ
Packing : Standard Export Packing
Port of Dispatch : It depends on the supplier's location and shipping arrangements
Delivery Time : The inventory is 5-7 days . 25-30 days for customized products
Payment : TT / LC / TT+LC
Alloy 1200 Composition: |
|
Aluminum (Al): | 99.0% |
Silicon (Si): | 0.05% |
Iron (Fe): | 0.05% |
Copper (Cu): | 0.05% |
Manganese (Mn): | 0.05% |
Others: | 0.05% (each), 0.15% (total) |