6101 Aluminium Sheet
Aluminum alloy 6101 is a high-conductivity alloy primarily used for electrical applications, such as bus bars and electrical conductors. It is known for its excellent electrical conductivity and good formability.
| Mechanical Properties: |
|---|
|
Tensile Strength: 25,000 psi (170 MPa) Yield Strength: 18,000 psi (125 MPa) Elongation: 12% |
| Physical Properties: |
|
Density: 2.70 g/cm³ (0.0975 lb/in³) Melting Range: 590°C-640°C (1094°F-1184°F) |
| Typical Uses: |
| Electrical conductors Bus bars Heat sinks for electronic devices Power distribution components Electrical connectors |
| Welding: |
| 6101 is readily weldable using standard methods such as gas metal arc welding (GMAW/MIG), gas tungsten arc welding (GTAW/TIG), and resistance welding. It responds well to fusion and resistance welding processes. |
| Corrosion Resistance: |
| 6101 has good corrosion resistance, particularly in indoor environments. However, its primary use in electrical applications often limits exposure to corrosive conditions. |
6101 Aluminium Sheets
Alloy : 6101 Aluminium Alloy
Temper :
O H14 H24 H18 / T351 T3 T4 T651 T6 / H14 H24 H26 H16 / H32 H111 H321 H116 H112 / T6 T651 / T651 T6 T7451
T61: Solution heat-treated and artificially aged.
Thickness : 0.2mm-300mm
Width : 500mm-3000mm
Standard : GB/ 3880-2012 ASTMB209 EN485
Surface Treatment : Mill finish / Brush polish
PVC Coated : One side or two side PVC
MOQ : The inventory has no MOQ
Packing : Standard Export Packing
Port of Dispatch : It depends on the supplier's location and shipping arrangements
Delivery Time : The inventory is 5-7 days . 25-30 days for customized products
Payment : TT / LC / TT+LC
Alloy 6061 Composition: |
|
| Aluminum (Al): | 98.9% |
| Silicon (Si): | 0.40%-0.80% |
| Iron (Fe): | 0.50% |
| Copper (Cu): | 0.30%-0.70% |
| Manganese (Mn): | 0.03% |
| Chromium (Cr): | 0.03% |
| Titanium (Ti): | 0.10% |
| Others: | 0.03% (each) 0.15% (total) |
Considerations: 6101 is known for its excellent electrical conductivity, which is a critical factor in its use for electrical applications. It is often chosen for applications where a combination of electrical conductivity and formability is required.